Processes
- Stereolithography (SLA)
Properties
- Rigid
- High strength
Colors
- White
Features
• Functional assemblies
• Short-run production parts
Post-Cured Material
MEASUREMENT | CONDITION | METRIC | U.S. |
Tensile Strength (MPa/PSI) | ASTM D 638 | 63-68 | 9200-9850 |
Tensile Modulus (MPa/KSI) | ASTM D 638 | 3200-3380 | 460-490 |
Elongation at Break (%) | ASTM D 638 | 5-8 % | 5-8 % |
Flexural Strength (MPa/PSI) | ASTM D 790 | 88-110 | 12830-15920 |
Flexural Modulus(MPa/KSI) | ASTM D 790 | 2690-3240 | 390-470 |
Impact Strength (J/m /Ft-lbs/in) | ASTM D 256 ASTM5420 | 12-22 1.1 |
0.2-0.4 0.81 |
Heat Deflection Temperature | ASTM D 648 @ 66 PSI @ 264 PSI |
55-58 °C 51-53 °C |
131-136 °F 123-127 °F |
Coefficient of Thermal Expansion (CTE) |
ASTM E 831-93 TMA (T<Tg, 0-40 °C) TMA (T<Tg, 75-140 °C) |
61 163 |
141 326 |
Glass Transition (Tg) | DMA, E” | 56 °C | 132 °F |
Shore D | 85 | 85 |
Liquid Material
MEASUREMENT | CONDITION | VALUE |
Viscosity | @ 30 °C (86 °F) | 155-185 cps |
Penetration Depth (Dp) | 5.2 mils | |
Critical Exposure (Ec) | 7.4 mJ/cm2 | |
Color | White | |
Solid Density | @ 25 °C (77 °F) | 1.20 g/cm3 at 25 °C |
Liquid Density | @ 25 °C (77 °F) | 1.13 g/cm3 at 25 °C |