Processes
- Stereolithography (SLA)
Properties
- Rigid
- High strength
Colors
- Clear
Finishes
- Natural
- Standard
- Paint-ready
- Painted
- Quick Clear
- Clearpart
- Custom
Features
• Great for investment casting patterns
• Headlamps, bottles and transparent assemblies
Post-Cured Material
MEASUREMENT | CONDITION | METRIC | U.S. |
Tensile Strength (MPa/PSI) | ASTM D 638 | 58-68 | 8410-9860 |
Tensile Modulus (MPa/KSI) | ASTM D 638 | 2690-3100 | 390-450 |
Elongation at Break (%) | ASTM D 638 | 5-13 % | 5-13 % |
Flexural Strength (MPa/PSI) | ASTM D 790 | 87-101 | 12620-14650 |
Flexural Modulus (MPa/KSI) | ASTM D 790 | 2700-3000 | 392-435 |
Impact Strength (J/m /Ft-lbs/in) | ASTM D 256 | 15-25 | 0.3-0.5 |
Heat Deflection Temperature | ASTM D 648 @ 66 PSI @ 264 PSI |
53-55 °C 48-50 °C |
127-131 °F 118-122 °F |
Coefficient of Thermal Expansion (CTE) |
ASTM E 831-93 TMA (T<Tg, 0-40 °C) TMA (T<Tg, 75-140 °C) |
71-131 153 |
|
Glass Transition (Tg) | DMA, E” | 58 °C | 136 °F |
Hardness, Shore D | 86 | 86 |
Liquid Material
MEASUREMENT | CONDITION | VALUE |
Viscosity | @ 30 °C (86 °F) | 150-180 cps |
Penetration Depth (Dp) | 6.3 mils | |
Critical Exposure (Ec) | 7.6 mJ/cm2 | |
Color | Clear | |
Solid Density | @ 25 °C (77 °F) | 1.21 g/cm3 at 25 °C |
Liquid Density | @ 25 °C (77 °F) | 1.13 g/cm3 at 25 °C |