Processes
- Stereolithography (SLA)
Properties
- Rigid
- Durable
Colors
- Clear
Finishes
- Natural
- Standard
- Paint-ready
- Painted
- Quick Clear
- Clearpart
- Custom
Features
• Headlamps, bottles and transparent assemblies
• Excellent humidity/moisture resistance
• Capable of meeting UPS Class VI
Post-Cured Material
MEASUREMENT | CONDITION | METRIC | U.S. |
Tensile Strength (MPa/PSI) | ASTM D 638 | 41-46 | 5950-6670 |
Tensile Modulus (MPa/KSI) | ASTM D 638 | 2030-2220 | 294-322 |
Elongation at Break (%) | ASTM D 638 | 4-7 | 4-6 |
Flexural Strength (MPa/PSI) | ASTM D 790 | 53-67 | 7690-9720 |
Flexural Modulus (MPa/KSI) | ASTM D 790 | 1560-2040 | 226-296 |
Impact Strength (J/m /Ft-lbs/in) | ASTM D 256 | 43-67 | 0.81-1.26 |
Heat Deflection Temperature | ASTM D 648 @ 66 PSI @ 264 PSI |
46 °C 41 °C |
115 °F 106 °F |
Coefficient of Thermal Expansion (CTE) |
ASTM E 831-93 < 35 °C > 60 °C |
70 160 |
70 160 |
Glass Transition (Tg) | DMA, E” | 56 °C | 133 °F |
Hardness, Shore D | 84 | 84 |
Liquid Material
MEASUREMENT | CONDITION | VALUE |
Viscosity | @ 30 °C (86 °F) | 235-260 cps |
Penetration Depth (Dp) | 6.1 mils | |
Critical Exposure (Ec) | 9.5 mJ/cm2 | |
Color | Clear | |
Solid Density | @ 25 °C (77 °F) | 1.17 g/cm3 |
Liquid Density | @ 28 °C (82 °F) | 1.10 g/cm3 |