Polycarbonate + ABS
Bayblend® FR3010
(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 110°C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; improved chemical resistance and stress cracking behavior; successor to FR2010
Processes
- Injection Mold Tooling & Parts
Colors
- White
- Gray
- Green
Features
- Chemical Resistant
- Flame Retardant
- High ESCR (Stress Crack Resist.)
- Medium Heat Resistance
Properties
General | ||||
Material Status
|
|
|||
Availability
|
|
|||
Additive
|
|
|||
Features
|
|
|||
|
||||
ISO Shortname
|
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density (73°F)
|
1.18
|
g/cm³
|
ISO 1183 |
Melt Volume-Flow Rate (MVR) (240°C/5.0 kg)
|
15
|
cm³/10min
|
ISO 1133 |
Molding Shrinkage 3
|
ISO 2577 | ||
Across Flow : 464°F, 0.118 in
|
0.50 to 0.70
|
%
|
|
Flow : 464°F, 0.118 in
|
0.50 to 0.70
|
%
|
|
Water Absorption
|
ISO 62 | ||
Saturation, 73°F
|
0.50
|
%
|
|
Equilibrium, 73°F, 50% RH
|
0.20
|
%
|
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Tensile Modulus (73°F)
|
392000
|
psi
|
ISO 527-1/1 |
Tensile Stress
|
ISO 527-2/50 | ||
Yield, 73°F
|
8700
|
psi
|
|
Break, 73°F
|
7250
|
psi
|
|
Tensile Strain
|
ISO 527-2/50 | ||
Yield, 73°F
|
4.0
|
%
|
|
Break, 73°F
|
> 50
|
%
|
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Deflection Temperature Under Load
|
|||
66 psi, Unannealed
|
212
|
°F
|
ISO 75-2/B |
264 psi, Unannealed
|
194
|
°F
|
ISO 75-2/A |
Vicat Softening Temperature
|
|||
—
|
230
|
°F
|
ISO 306/B120 |
—
|
226
|
°F
|
ISO 306/B50 |
CLTE
|
ISO 11359-2 | ||
Flow : 73 to 131°F
|
4.2E-5
|
in/in/°F
|
|
Transverse : 73 to 131°F
|
4.4E-5
|
in/in/°F
|
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Surface Resistivity
|
1.0E+16
|
ohms
|
IEC 60093 |
Volume Resistivity (73°F)
|
1.0E+16
|
ohms·cm
|
IEC 60093 |
Electric Strength (73°F, 0.0394 in)
|
890
|
V/mil
|
IEC 60243-1 |
Relative Permittivity
|
IEC 60250 | ||
73°F, 100 Hz
|
3.20
|
||
73°F, 1 MHz
|
3.10
|
||
Dissipation Factor
|
IEC 60250 | ||
73°F, 100 Hz
|
5.0E-3
|
||
73°F, 1 MHz
|
7.0E-3
|
||
Comparative Tracking Index (Solution A)
|
350
|
V
|
IEC 60112 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating
|
UL 94 | ||
0.06 in
|
V-0
|
||
0.08 in
|
5VB
|
||
0.12 in
|
5VA
|
||
Oxygen Index 4
|
32
|
%
|
ISO 4589-2 |
Fill Analysis |
Nominal Value
|
Unit
|
Test Method
|
Melt Viscosity 4 (500°F)
|
245
|
Pa·s
|
ISO 11443-A |
Injection |
Nominal Value
|
Unit
|
|
Drying Temperature – Dry Air Dryer
|
176
|
°F
|
|
Drying Time – Dry Air Dryer
|
4.0
|
hr
|
|
Suggested Max Moisture
|
< 0.020
|
%
|
|
Suggested Shot Size
|
30 to 70
|
%
|
|
Rear Temperature
|
428 to 446
|
°F
|
|
Middle Temperature
|
437 to 455
|
°F
|
|
Front Temperature
|
446 to 464
|
°F
|
|
Nozzle Temperature
|
491 to 509
|
°F
|
|
Processing (Melt) Temp
|
464 to 518
|
°F
|
|
Mold Temperature
|
140 to 194
|
°F
|
|
Back Pressure
|
725 to 2180
|
psi
|
|
Vent Depth
|
9.8E-4 to 3.0E-3
|
in
|
Notes |
2150x105x3mm,, MT 80°C |
3Procedure A |
41000s-1 |