Thermoplastic Vulcanizate
Santoprene 101-64
A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene® TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion or blow molding. It is polyolefin based and recyclable within the manufacturing stream.
Processes
- Injection Mold Tooling & Parts
Properties
- Flexible
Colors
- Black
Applications
- Appliance Components
- Automotive Applications
- Automotive Bumper
- Automotive Under the Hood
- Blow Molding Applications
- Consumer Applications
- Diaphragms
- Electrical Parts
- Electrical/Electronic Applications
- Gaskets
- Grommets
- Outdoor Applications
Properties
General | ||||
Material Status
|
|
|||
Availability
|
|
|||
Uses
|
|
|||
Agency Ratings
|
|
|||
UL File Number
|
|
|||
Appearance
|
|
|||
Forms
|
|
|||
Processing Method
|
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density / Specific Gravity
|
|||
—
|
0.972
|
ASTM D792 | |
—
|
0.970
|
g/cm³
|
ISO 1183 |
Outdoor Suitability
|
f1
|
UL 746C | |
Detergent Resistance
|
f4
|
UL 2157 | |
Detergent Resistance
|
f3
|
UL 749 |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Brittleness Temperature
|
-76.0
|
°F
|
ASTM D746, ISO 812 |
RTI Elec
|
194
|
°F
|
UL 746B |
RTI Str
|
UL 746B | ||
0.04 in
|
194
|
°F
|
|
0.06 in
|
194
|
°F
|
|
0.12 in
|
203
|
°F
|
Electrical |
Nominal Value
|
Unit
|
Test Method
|
Volume Resistivity
|
ASTM D257 | ||
0.0787 in
|
1.0E+16
|
ohms·cm
|
|
0.126 in
|
5.0E+15
|
ohms·cm
|
|
Dielectric Strength (0.0787 in)
|
690
|
V/mil
|
ASTM D149 |
Dielectric Constant (0.0780 in, 60 Hz)
|
2.50
|
ASTM D150, IEC 60250 | |
Comparative Tracking Index (CTI)
|
PLC 0
|
UL 746A | |
High Amp Arc Ignition (HAI)
|
PLC 0
|
UL 746A | |
High Voltage Arc Resistance to Ignition (HVAR)
|
PLC 6
|
UL 746A | |
High Voltage Arc Tracking Rate (HVTR)
|
PLC 1
|
UL 746A | |
Hot-wire Ignition (HWI)
|
PLC 2
|
UL 746A |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Flame Rating
|
UL 94 | ||
0.04 in
|
HB
|
||
0.06 in
|
HB
|
||
0.12 in
|
HB
|
Aging |
Nominal Value
|
Unit
|
Test Method
|
Change in Tensile Strength in Air (302°F, 168 hr)
|
-9.4
|
%
|
ASTM D573, ISO 188 |
Change in Ultimate Elongation in Air (302°F, 168 hr)
|
-7.7
|
%
|
ASTM D573, ISO 188 |
Change in Durometer Hardness in Air (Shore A, 302°F, 168 hr)
|
1.3
|
ASTM D573, ISO 188 | |
Continuous Upper Temperature Resistance (1008 hr)
|
275
|
°F
|
SAE J2236 |
Elastomers |
Nominal Value
|
Unit
|
Test Method
|
Tensile Stress – Across Flow (100% Strain)
|
410
|
psi
|
ASTM D412, ISO 37 |
Tensile Strength – Across Flow (Break)
|
938
|
psi
|
ASTM D412, ISO 37 |
Tensile Elongation – Across Flow (Break)
|
450
|
%
|
ASTM D412, ISO 37 |
Tear Strength – Across Flow 3
|
131
|
lbf/in
|
ISO 34-1 |
Compression Set
|
|||
158°F, 22 hr 4
|
25
|
%
|
ASTM D395B |
257°F, 70 hr 4
|
44
|
%
|
ASTM D395B |
158°F, 22 hr 5
|
25
|
%
|
ISO 815 |
257°F, 70 hr 5
|
44
|
%
|
ISO 815 |
Injection |
Nominal Value
|
Unit
|
|
Drying Temperature
|
180
|
°F
|
|
Drying Time
|
3.0
|
hr
|
|
Suggested Max Moisture
|
0.080
|
%
|
|
Suggested Max Regrind
|
20
|
%
|
|
Rear Temperature
|
351
|
°F
|
|
Middle Temperature
|
360
|
°F
|
|
Front Temperature
|
360
|
°F
|
|
Nozzle Temperature
|
370 to 430
|
°F
|
|
Processing (Melt) Temp
|
379 to 450
|
°F
|
|
Mold Temperature
|
50 to 126
|
°F
|
|
Injection Rate
|
Fast
|
||
Back Pressure
|
50.0 to 99.9
|
psi
|
|
Screw Speed
|
100 to 200
|
rpm
|
|
Clamp Tonnage
|
3.0 to 5.0
|
tons/in²
|
|
Cushion
|
0.125 to 0.250
|
in
|
|
Screw L/D Ratio
|
16.0:1.0 to 20.0:1.0
|
||
Screw Compression Ratio
|
2.0:1.0 to 2.5:1.0
|
||
Vent Depth
|
9.8E-4
|
in
|
Notes |
3Method Ba, Angle (Unnicked) |
4Type 1 |
5Type A |